Год выпуска: 2011 Автор: Ashwin Padmanaban Iyer Издательство: LAP Lambert Academic Publishing Страниц: 72 ISBN: 9783847304579
Описание
The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion methodology where a coupon (material under study, in this case a rectangular stainless steel specimen of SS304 with dimensions approximately 5X20X.6mm and weight .5gm) is exposed to a static corroding environment for predetermined periods of time. The testing times were 2, 4 and 6 weeks. The temperature during testing was maintained at a constant 520C. The instantaneous corrosion rates were determined by normalizing the mass loss with respect to time and area. The mass loss was determined by descaling the corroded steel coupons using concentrated hydrochloric acid. The instantaneous corrosion rates obtained from all three times showed a reduction in corrosion of steel by molten carbonate eutectics when doped with silica 1% by weight in comparison to the molten base carbonate eutectics. The results...
По диплому вопросов больше нет, все благополучно сдано. Жена счастлива. Соответственно и я!) Получила ХОРОШО, но это видимо из-за причуд преподавателей. Кому-то ведь надо ставить 4, а кому-то 5). Я чего пишу то, хочу сказать вам огромное спасибо за вашу работу!!! Хорошо что есть такие люди, которые могут вовремя прийти на помощь. Мы в силу своей занятости иногда не можем справится с тем, что надо, тут и помогают такие люди, как вы). СПАСИБО ОГРОМНОЕ! Будем вас советовать другим лицам, находящимся в таком же положении!